> Products > Pii Carbide Coated > Barrel Susceptor > SiC Coated Graphite Ferocactus Susceptor

Products

New Products

SiC Coated Graphite Ferocactus Susceptor

Si quaeris summus graphite susceptor usus in semiconductor applicationis fabricandi, Semicorex SiC Coated Graphite Barrel Susceptor est specimen electionis. Eximia scelerisque conductivity et calorum distributio proprietatibus eam eligit ad certas et constantes observantias in ambitus magnos temperaturae et mordax.

Mitte Inquisitionem

depictio producti

Semicorex SiC Coated Graphite Ferocactus Susceptor est perfecta electio pro semiconductor applicationes fabricandi quae requirunt eximiam caloris distributionem et conductivity scelerisque. Eius summus puritas SiC coating et densitas superior tutelam et calorem superiorum praebent proprietates distributionis, certas et constantes effectus in ambitibus etiam gravissimis praestando.

Nostrum SiC Coated Graphite Ferocactus Susceptor designatus est ad optimam laminae gasi fluens exemplar consequendum, aequabilitatem de profile scelerisque procurando. Hoc adiuvat ne quis contagione vel immunditiae diffusionem praestet, ut summus qualitas incrementi epitaxialis in lagano chip.

Contactus nos hodie ut plura discamus de Graphite Barrel Susceptore nostro SiC Coated.

Parametri Sic Coated Graphite Ferocactus Susceptor

Specificationes principales de CVD-SIC Coating .
Sic-CVD Properties
Crystal Structure	FCC β phase
Densitas	g/cm	3.21
duritia	Vickers duritia	2500
Frumenti Size	μm	2~10
Puritas chemica	%	99.99995
Calor Capacity	J kg-1 K-1	640
Sublimatio Temperature	℃	2700
Fortitudo Felix	MPa (RT 4-punctum)	415
Modulus	Gpa (4pt bend, 1300℃)	430
Scelerisque Expansion (C.T.E)	10-6K-1	4.5
Scelerisque conductivity	(W/mK)	300

Features of Sic Coated Graphite Ferocactus Susceptor

- Tum graphite substrato et carbidi pii strato densitatem bonam habent et bonam munus tutelae in cultura caliditatis ac mordax operandi ambitibus ludere possunt.

- Silicon carbide obductis susceptoribus adhibitis pro incremento crystalli unius habet praealtissimae superficiei planiciem.

- Reducere differentiam in expansione scelerisque coëfficientis inter graphite substrato et carbide pii strato, efficaciter meliores compages vires ne crepuit et delaminatio.

- Tam graphite substratum et carbide pii stratum altum scelerisque conductivity habent, et caloris excellentia proprietates distributio.

- Maximum punctum liquescens, caliditas oxidationis resistentia, corrosio resistentia.